Corrosion behavior of Zinc or 55%Al-Zn hot-dip coated steel in 0.5 m NaCl solution

M.Granada, P.R.Ser�?�?�?�?�?�?�?©, C.I.Elsner, A.R.Di Sarli


Acomparative study on the anticorrosive behaviour of 55%Aluminum-Zincalloy and Zinc hot-dip coated carbon steel immersed in 0.5 mol/L NaCl solution was performed using DC (polarization curves) and AC (electrochemical impedance spectroscopy) techniques. Also, the corrosion products formed under these testing conditions were characterized using XRD, SEM and EDS. The experimental results showed that the corrosion resistance of the 55%Al-Zn alloy coating showed a synergistic effect being more satisfactory than the each metal used separately and the Zn tested coating. This was attributed to the effectiveness of two forms of protection: the cathodic protection and the barrier effect (afforded by a basic zincaluminumcarbonate layer) acting together. Themorphological characteristics of their corrosion products also differed.


インデックス付き

  • キャス
  • Google スカラー
  • Jゲートを開く
  • 中国国家知識基盤 (CNKI)
  • サイテファクター
  • コスモスIF
  • 電子ジャーナルライブラリ
  • 研究ジャーナル索引作成ディレクトリ (DRJI)
  • 秘密検索エンジン研究所
  • ICMJE

もっと見る

ジャーナルISSN

ジャーナル h-インデックス

Flyer

オープンアクセスジャーナル